PA66

TEST ITEMS

TEST METHOD AND CONDITIONS

RESULTS

TEST METHOD

UNIT

CONDITION (DRY)23

Density

ISO1183

g/cm3

1.1

Melt Volume Rate

ISO1133

cc/10min

(275)2.16kg

43.2

Tensile Strength

ISO527

MPa

10mm/min

67.8

Tensile strain at break

ISO527

%

5

Flexural Modulus

ISO178

MPa

2,800

Flexural Strength 

ISO178

MPa

2mm/min

82

Charpy Notched

ISO179

KJ/m2

2.9m/s-1J

11

Izod Notched Impact

ISO180

KJ/m2

3.5m/s-1J

8.6

Flame resistance

UL-94

V-0